What you’re describing are different crystalline phases of pure compounds, but this does not give you new minima, you need some new compound to form for that
In normal cases you’d see two curves going away from pure compounds downwards to a common minimum, which is eutectic point. It’s generally only vaguely predictable, but always monotonic